玻璃纤维增强材料, PTFE润滑剂, 良好的抗蠕变性, 抗溶解性, 耐磨蚀性, 收缩性低, 阻燃, 医疗/护理

 

China PPS PTFE-hGR302

聚苯硫醚

Sichuan Deyang Chemical Co., Ltd

Technical Data

 

产品说明

 

PPS/PTFE-hGR302 is lubricant PPS compound, which is filled with glass fiber, PTFE and ingredients based on the PPS resin. It shows abrasive resistance, solvent resistance and good mechanic prosperity, high modulus, creep resistance, high-temperature resistance, inherent flame resistance, easy processing, low mold shrinkage.

 

Owing to its high performance, it's widely used in mechanical and chemical industry for making wearable parts/components which work in the high-temperature, high pressure and solvent circumstance. It's also an excellent candidate in aerospace field.

 

总体

 

材料状态 • 已商用：当前有效

资料 1 •  Technical Datasheet (English)

搜索 UL 黄卡 •  Sichuan Deyang Chemical Co., Ltd

 

供货地区 • 亚太地区

填料/增强材料 • 玻璃纤维增强材料

添加剂 • PTFE润滑剂

• 经润滑 • 良好的抗蠕变性 • 耐热性，高

性能特点 • 抗溶解性 • 耐磨蚀性，良好 • 收缩性低

• 可加工性，良好 • 耐磨损性良好 • 阻燃性能

用途 • 工业领域： • 航空航天应用

加工方法 • 注射成型

 

物理性能 额定值单位制 测试方法

密度 1.58g/cm³ Internal Method

收缩率 - 流动 0.25% Internal Method

机械性能 额定值单位制 测试方法

抗张强度 136MPa Internal Method

弯曲模量 10000MPa Internal Method

弯曲强度 200MPa Internal Method

摩擦系数 0.40 Internal Method

Abrasion - Width 6mm Internal Method

磨损量 3 6.0mg Internal Method

冲击性能 额定值单位制 测试方法

悬壁梁缺口冲击强度 13kJ/m² Internal Method

热性能 额定值单位制 测试方法

热变形温度 (1.8 MPa, 未退火) 272°C Internal Method

注射 额定值单位制

干燥温度 110 到 140°C

干燥时间 3.0 到 5.0hr

螺筒后部温度 270 到 290°C

螺筒中部温度 300 到 320°C

螺筒前部温度 300 到 320°C

射嘴温度 290 到 320°C

加工（熔体）温度 160 到 180°C

模具温度 100 到 150°C

注塑温度 50.0 到 100MPa

背压 0.100 到 1.00MPa

螺杆转速 40 到 100rpm

注射说明

Processing time: 6 to 12hr

 

 

 

 