AvaSpire® AV-621 CF30

 

Polyaryletherketone

 

Solvay Specialty Polymers

 

Technical Data

 

Product Description

 

AvaSpire® AV-621 CF30 is a 30% carbon fiber reinforced version of AvaSpire® AV-621. It offers better dimensional stability and warp resistance than 30% carbon fiber reinforced PEEK. The AV-621 CF30 grade offers the highest strength, stiffness, and fatigue resistance of any AV-621 based grade. Furthermore, this resin generally retains most of the desirable ultra-performance attributes of carbon fiber reinforced PEEK including chemical resistance, fatigue resistance, and long term thermal oxidative stability.

 

The excellent balance of properties of AV-621 CF30 makes this grade well suited for a broad range of applications across a number of industries, including healthcare, transportation, electronics, and chemical processing.

 

This resin can be easily melt processed by injection molding using standard equipment. The melt processing behavior of AV-621 CF30 is very similar to that of 30% CF reinforced PEEK. The lower melt flow of AV-621 CF30 is well suited for extrusion applications while offering a similar property profile to AV-651 CF30.

 

General

 

Material Status • Commercial: Active

Literature 1 • Technical Datasheet

Search for UL Yellow Card • Solvay Specialty Polymers

• AvaSpire®

Availability • Africa & Middle East • Europe • North America

• Asia Pacific • Latin America

Filler / Reinforcement • Carbon Fiber, 30% Filler by Weight

• Fatigue Resistant • Good Dimensional Stability

Features • Flame Retardant • High Heat Resistance • High Strength

• Good Chemical Resistance • High Stiffness

Uses • Medical/Healthcare • Pump Parts • Seals

Applications

RoHS Compliance • Contact Manufacturer

Appearance • Black

Forms • Pellets

Processing Method • Injection Molding • Machining • Profile Extrusion

 

Physical Nominal Value (English) Nominal Value (SI) Test Method

Specific Gravity 1.42 1.42 g/cm³ ASTM D792

Melt Mass-Flow Rate (MFR) (400°C/2.16 kg) 1.0 g/10 min 1.0 g/10 min ASTM D1238

Molding Shrinkage 3 ASTM D955

Flow : 0.125 in (3.18 mm) 0.0 to 2.0E-3 in/in 0.0 to 0.20 %

Across Flow : 0.125 in (3.18 mm) 9.0E-3 to 0.011 in/in 0.90 to 1.1 %

Water Absorption (24 hr) 0.10 % 0.10 % ASTM D570

Mechanical Nominal Value (English) Nominal Value (SI) Test Method

Tensile Modulus

-- 4 2.49E+6 psi 17200 MPa ASTM D638

-- 3.38E+6 psi 23300 MPa ISO 527-2/1A/1

Tensile Stress

Yield 28400 psi 196 MPa ISO 527-2/1A/5

-- 4 26300 psi 181 MPa ASTM D638

Tensile Elongation

Break 4 2.2 % 2.2 % ASTM D638

Break 2.2 % 2.2 % ISO 527-2/1A/5

Flexural Modulus

-- 2.19E+6 psi 15100 MPa ASTM D790

-- 3.09E+6 psi 21300 MPa ISO 178

 

AvaSpire® AV-621 CF30

Polyaryletherketone

Solvay Specialty Polymers

Mechanical Nominal Value (English) Nominal Value (SI) Test Method

Flexural Strength

-- 40100 psi 276 MPa ASTM D790

-- 42900 psi 296 MPa ISO 178

Compressive Strength 22000 psi 152 MPa ASTM D695

Shear Strength 13200 psi 91.0 MPa ASTM D732

Impact Nominal Value (English) Nominal Value (SI) Test Method

Notched Izod Impact

-- 1.3 ft•lb/in 69 J/m ASTM D256

-- 4.6 ft•lb/in² 9.6 kJ/m² ISO 180

Unnotched Izod Impact

-- 12 ft•lb/in 640 J/m ASTM D4812

-- 19 ft•lb/in² 39 kJ/m² ISO 180

Hardness Nominal Value (English) Nominal Value (SI) Test Method

Rockwell Hardness (M-Scale) 101 101 ASTM D785

Thermal Nominal Value (English) Nominal Value (SI) Test Method

Deflection Temperature Under Load 5 ASTM D648

264 psi (1.8 MPa), Annealed, 0.126 in (3.20 410 °F 210 °C

mm)

Glass Transition Temperature 320 °F 160 °C ASTM D3418

Peak Melting Temperature 644 °F 340 °C ASTM D3418

CLTE - Flow (-58 to 122°F (-50 to 50°C)) 2.8E-6 in/in/°F 5.0E-6 cm/cm/°C ASTM E831

Specific Heat DSC

122°F (50°C) 0.323 Btu/lb/°F 1350 J/kg/°C

392°F (200°C) 0.433 Btu/lb/°F 1810 J/kg/°C

Thermal Conductivity 2.4 Btu•in/hr/ft²/°F 0.35 W/m/K ASTM E1530

Fill Analysis Nominal Value (English) Nominal Value (SI) Test Method

Melt Viscosity (752°F (400°C), 1000 sec^-1) 790 Pa•s 790 Pa•s ASTM D3835

Injection Nominal Value (English) Nominal Value (SI)

Drying Temperature 300 °F 149 °C

Drying Time 4.0 hr 4.0 hr

Rear Temperature 690 °F 366 °C

Middle Temperature 700 °F 371 °C

Front Temperature 710 °F 377 °C

Nozzle Temperature 720 °F 382 °C

Processing (Melt) Temp 690 to 730 °F 366 to 388 °C

Mold Temperature 300 to 350 °F 149 to 177 °C

Injection Rate Fast Fast

Screw Compression Ratio 2.0:1.0 to 3.0:1.0 2.0:1.0 to 3.0:1.0

Injection Notes

Back Pressure: Minimum

 

 

 

 

 