VICTREX® PEEK 150FW30

 

Polyetheretherketone

 

Victrex plc

 

Technical Data

 

Product Description

 

High performance thermoplastic material, 30% reinforced with carbon fibre / PTFE PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection moulding, easy flow, FDA food contact compliant, colour black.

 

Tribological applications with thin cross sections or long flow lengths for high strength. Excellent wear resistance, very low coefficient of friction, low coefficient of thermal expansion. Chemically resistant to aggressive environments.

 

General

 

Material Status • Commercial: Active

 

• Brochure - Chemical Resistance (English) 

• Processing - Victrex PEEK Compression Molding Guide (English) 

Literature 1 • Processing - Victrex PEEK Extrusion Guide (English)

Processing - Victrex PEEK Finishing Operations (English)

•

• Processing - Victrex PEEK Injection Molding Guide (English)

• Technical Datasheet (English)

Search for UL Yellow Card • Victrex plc

• VICTREX® PEEK

Availability • Asia Pacific • Europe • North America

Filler / Reinforcement • Carbon\PTFE, 30% Filler by Weight

• Food Contact Acceptable • Good Wear Resistance

Features • Good Chemical Resistance • High Strength • Semi Crystalline

• Good Flow • Low Friction

Agency Ratings • FDA Food Contact, Unspecified Rating

Appearance • Black

Forms • Granules

Processing Method • Injection Molding

Physical Nominal Value (English) Nominal Value (SI) Test Method

Density 3 1.43 g/cm³ 1.43 g/cm³ ISO 1183

Spiral Flow 4, 5 6.50 in 16.5 cm Internal Method

Molding Shrinkage 6 ISO 294-4

Across Flow : 356°F (180°C) 0.60 % 0.60 %

Flow : 356°F (180°C) 0.10 % 0.10 %

Water Absorption ISO 62

73°F (23°C), 24 hr, 0.126 in (3.20 mm) 0.040 % 0.040 %

Equilibrium, 73°F (23°C), 0.126 in (3.20 mm), 0.30 % 0.30 %

50% RH

Mechanical Nominal Value (English) Nominal Value (SI) Test Method

Tensile Modulus (73°F (23°C)) 2.18E+6 psi 15000 MPa ISO 527-2

Tensile Stress ISO 527-2

Break, 73°F (23°C) 26100 psi 180 MPa

Break, 257°F (125°C) 16700 psi 115 MPa

Tensile Strain (Break, 73°F (23°C)) 1.8 % 1.8 % ISO 527-2

Flexural Modulus (73°F (23°C)) 2.10E+6 psi 14500 MPa ISO 178

Flexural Stress ISO 178

73°F (23°C) 39200 psi 270 MPa

257°F (125°C) 24700 psi 170 MPa

347°F (175°C) 14500 psi 100 MPa

437°F (225°C) 8700 psi 60.0 MPa

Compressive Stress ISO 604

73°F (23°C) 30500 psi 210 MPa

248°F (120°C) 22500 psi 155 MPa

392°F (200°C) 8700 psi 60.0 MPa

 

VICTREX® PEEK 150FW30

 

Polyetheretherketone

 

Victrex plc

Impact Nominal Value (English) Nominal Value (SI) Test Method

Charpy Notched Impact Strength (73°F (23°C)) 2.4 ft•lb/in² 5.0 kJ/m² ISO 179/1eA

Charpy Unnotched Impact Strength ISO 179/1U

73°F (23°C) 17 ft•lb/in² 35 kJ/m²

Notched Izod Impact Strength (73°F (23°C)) 2.4 ft•lb/in² 5.0 kJ/m² ISO 180/A

Unnotched Izod Impact Strength (73°F (23°C)) 17 ft•lb/in² 35 kJ/m² ISO 180

Hardness Nominal Value (English) Nominal Value (SI) Test Method

Shore Hardness (Shore D, 73°F (23°C)) 85 85 ISO 868

Thermal Nominal Value (English) Nominal Value (SI) Test Method

Heat Deflection Temperature ISO 75-2/Af

264 psi (1.8 MPa), Unannealed 617 °F 325 °C

Glass Transition Temperature 289 °F 143 °C ISO 11357-2

Melting Temperature 649 °F 343 °C ISO 11357-3

CLTE ISO 11359-2

Flow : > 289°F (> 143°C) 5.0E-5 in/in/°F 9.0E-5 cm/cm/°C

Flow : < 289°F (< 143°C) 5.0E-5 in/in/°F 9.0E-5 cm/cm/°C

Transverse : < 289°F (< 143°C) 2.5E-5 in/in/°F 4.5E-5 cm/cm/°C

Transverse : > 289°F (> 143°C) 6.1E-5 in/in/°F 1.1E-4 cm/cm/°C

Specific Heat Capacity 4.30E-4 Btu/lb/°F 1.80 J/kg/°C DSC

Electrical Nominal Value (English) Nominal Value (SI) Test Method

Volume Resistivity 7 (73°F (23°C)) 1.0E+7 ohms•cm 1.0E+7 ohms•cm IEC 60093

Fill Analysis Nominal Value (English) Nominal Value (SI) Test Method

Melt Viscosity (752°F (400°C)) 260 Pa•s 260 Pa•s ISO 11443

Injection Nominal Value (English) Nominal Value (SI)

Drying Temperature 248 to 302 °F 120 to 150 °C

Drying Time 3.0 to 5.0 hr 3.0 to 5.0 hr

Hopper Temperature < 212 °F < 100 °C

Rear Temperature 689 °F 365 °C

Middle Temperature 698 to 707 °F 370 to 375 °C

Front Temperature 716 °F 380 °C

Nozzle Temperature 725 °F 385 °C

Mold Temperature 338 to 392 °F 170 to 200 °C

Injection Notes

Runner: Die / nozzle >3mm, manifold >3.5mm

 

Gate: >2mm or 0.5 x part thickness

 

 

 

 

 